Forest of semiconducting nanowires for thermoelectricity

Abstract : Thermoelectric conversion has gained renewed interest based on the possibilities of increasing the efficiencies while exploiting the size effects. For instance, nanowires theoretically show increased power factors along with reduced phonon transport owing to confinement and/or size effects. In this context, the diameter of the nanowires becomes a crucial parameter to address in order to obtain high thermoelectric efficiencies. A usual approach is directed towards reducing the phononic thermal conductivity in nanowires by achieving enhanced boundary scattering while reducing diameters.In this work, thermal characterisation of a dense forest of silicon, germanium, silicon-germanium and Bi2Te3 alloy nanowires is done through a sensitive 3ω method. These forest of nanowires for silicon, germanium and silicon-germanium alloy were grown through bottom-up technique following the Vapour-Liquid-Solid mechanism in Chemical vapour deposition. The template-assisted and gold catalyst growth of nanowires with controlled diameters was achieved with the aid of tuneable nanoporous alumina as templates. The nanowires are grown following the internal geometry of the nanopores, in such a case the surface profile of the nanowires can be modified according to the fabricated geometry of nanopores. Benefiting from this fact, high-density growth of diameter-modulated nanowires was also demonstrated, where the amplitude and the period of modulation can be easily tuned during the fabrication of the templates. Even while modulating the diameters during growth, the nanowires were structurally characterised to be monocrystalline through transmission electron microscopy and X-ray diffraction analysis.The thermal characterisation of these nanowires revealed a strong diameter dependent decrease in the thermal conductivity, where the reduction was predominantly linked to strong boundary scattering. The mean free path contribution to the thermal conductivity observed in the bulk of fabricated nanowire materials vary a lot, where Bi2Te3 has strikingly low mean free path distribution (0.1 nm to 15 nm) as compared to the other materials. Even then, reduced thermal conductivities (~40%) were observed in these alloys attributed to boundary and impurity scattering. On the other hand, silicon and germanium have higher thermal conductivity with a larger mean free path distribution. In these nanowires, a significant reduction (10-15 times) was observed with a strong dependence on the size of the nanowires.While size effects reduce the thermal conductivity by enhanced boundary scattering, doping these nanowires can incorporate mass-difference scattering at atomic length scales. The temperature dependence of thermal conductivity was determined for doped nanowires of silicon to observe a reduction in thermal conductivity to a value of 4.6 W.m-1K-1 in highly n-doped silicon nanowires with 38 nm diameter. Taking into account the electrical conductivity and calculated Seebeck coefficient, a ZT of 0.5 was observed. With these significant increase in the efficiency of silicon as a thermoelectric material, a real practical application to devices is not far from reality.
Complete list of metadatas

Cited literature [543 references]  Display  Hide  Download

https://tel.archives-ouvertes.fr/tel-02390464
Contributor : Abes Star <>
Submitted on : Tuesday, December 3, 2019 - 10:08:20 AM
Last modification on : Monday, December 9, 2019 - 10:16:06 AM

File

SINGHAL_2019_diffusion.pdf
Version validated by the jury (STAR)

Identifiers

  • HAL Id : tel-02390464, version 1

Collections

STAR | UGA | CEA | IRIG | CNRS | NEEL | CEA-GRE

Citation

Dhruv Singhal. Forest of semiconducting nanowires for thermoelectricity. Mesoscopic Systems and Quantum Hall Effect [cond-mat.mes-hall]. Université Grenoble Alpes, 2019. English. ⟨NNT : 2019GREAY016⟩. ⟨tel-02390464⟩

Share

Metrics

Record views

88

Files downloads

186