Diamond-based multimaterials for thermal management applications

Abstract : Today, the microelectronics industry uses higher functioning frequencies in commercialized components. These frequencies result in higher functioning temperatures and, therefore, limit a component’s integrity and lifetime. Until now, heat-sink materials were composed of metals which exhibit high thermal conductivities (TC). However, these metals often induce large coefficient of thermal expansion (CTE) mismatches between the heat sink and the nonmetallic components of the device. Such differences in CTEs cause thermomechanical stresses at the interfaces and result in component failure after several on/off cycles.To overcome this issue, we suggest replacing the metallic heat sink materials with a heat-spreader (diamond film) deposited on metal matrix composites (MMCs), specifically, carbon-reinforced copper matrices (Cu/C) which exhibit optimized thermomechanical properties. However, proper transfer of properties in MMCs is often compromised by the absence of effective interfaces, especially in nonreactive systems such as Cu/C. Therefore, the creation of a chemical bond is ever more relevant. The goal of this research was to combine the exceptional properties of diamond by means of a thin film and the adaptive thermomechanical properties of MMCs. Carbon-reinforced copper matrix composites were synthesized using an innovative solid-liquid coexistent phase process to achieve designed composition gradients and optimized matrix/reinforcement interface properties. In addition, the lack of chemical affinitybetween Cu and C results in poor thermal efficiency of the composites. Therefore, alloying elements were inserted into the material to form carbide interphases at the Cu/C interface. Their addition enabled the composite’s integrity to be optimized in order to obtain thermally efficient assemblies. The diamond, in the form of a thin layer, was obtained by laser-assisted chemical vapor deposition. This process allowed action on the film’s phase purity and adhesion to the substrate material. Of particular importance was the influence of the interfaces on thermal properties both within the composite material (matrix-reinforcement interface) and within the diamond film-MMC assembly. This work was carried out within the framework of a Franco-American agreement between the Institute of Condensed Matter Chemistry of the University of Bordeaux in France and the Department of Electrical Engineering at the University of Nebraska-Lincoln, in the United States. Funding, in France, was provided by the Direction Générale de l’Armement (DGA), and by the American equivalent in the United States.
Document type :
Theses
Complete list of metadatas

https://tel.archives-ouvertes.fr/tel-01699064
Contributor : Abes Star :  Contact
Submitted on : Friday, February 2, 2018 - 1:05:28 AM
Last modification on : Tuesday, May 26, 2020 - 3:05:22 AM
Long-term archiving on: : Wednesday, May 2, 2018 - 3:46:12 PM

File

AZINA_CLIO_2017.pdf
Version validated by the jury (STAR)

Identifiers

  • HAL Id : tel-01699064, version 1

Collections

Citation

Clio Azina. Diamond-based multimaterials for thermal management applications. Material chemistry. Université de Bordeaux; University of Nebraska-Lincoln, 2017. English. ⟨NNT : 2017BORD0767⟩. ⟨tel-01699064⟩

Share

Metrics

Record views

725

Files downloads

393