Structural approach and ionic conductivity study of lithium thioarsenite based glasses and mixed former glasses with lithium thioborate and thioarsenite
Approche structurale et étude de la conduction ionique de verres a base de thioarsenite de lithium et de verres a formateur mixte, thioborate et thioarsenite de lithium
Résumé
A new family of glasses of the As2S3-Li2S-Lil system was studied. They exhibit high ionic conductivity. A study of the local order using different techniques made it possible to propose structural hypotheses. The crystallographic study of a new compound Li3AsS3 also allowed a comparative structural study with glass of the same composition. The evolution of the physical properties of these glasses (ionic conductivity, glass transition temperature, density) was correlated to their compositions. A small glassy domain was highlighted in the As2S3-B2S3-Li2S system comprising two forming sulphides. The characterization of these materials made it possible to propose structural hypotheses linked to their homogeneity.
Une nouvelle famille de verres du système As2S3-Li2S-Lil a été étudiée. Ils présentent une conductivité ionique élevée. Une étude de l'ordre local par différentes techniques a permis de proposer des hypothèses structurales. L'étude cristallographique d'un nouveau compose Li3AsS3 a permis, d'autre part, une étude structurale comparative avec le verre de même composition. L'évolution des propriétés physiques de ces verres (conductivité ionique, température de transition vitreuse, densité), a été correlée a leurs compositions. Un petit domaine vitreux a été mis en évidence dans le système As2S3-B2S3-Li2S comportant deux sulfures formateurs. La caractérisation de ces matériaux a permis de proposer des hypothèses structurales liées a leur homogènéité.