Determination of crystal and magnetic structures using neutron diffraction: application to AxM2(PO4)3 phosphates and to transition metal fluorides
Détermination de structures cristallines et magnétiques par diffraction neutronique : application aux phosphates de types AxM2(PO4)3 et à des fluorures magnétiques
Résumé
The structures of AxM2(PO4)3 (x=0.5, A=Mg, Co, Cu M=Zr, Ti; x=1 M=Cu) and Cu21CrZr(PO4)3 phosphates were determined by X-ray diffraction and neutron diffraction. The monovalent copper phases are characterized by the presence of CuI-CuI pairs. The crystal and magnetic structures of several series of ternary transition element fluorides have been determined. The structures are formed by a lattice of MF6 octahedra linked together in 3D, 2D or 1D. Magnetic structures were determined either in the absence of a magnetic field, or at a field strength of up to 6T. Spin-flop transitions characterize the compounds TIMnIIIF4, xH2O (x=0.1). A new structural variety of weberite has been characterized.
Les structures des phosphates de type AxM2(PO4)3 (x=0,5, A=Mg, Co, Cu M=Zr, Ti; x=1 M=Cu) et de Cu21CrZr(PO4)3 ont été déterminées par diffraction des rayons X et par diffraction des neutrons. Les phases du cuivre monovalent sont remarquables par la mise en évidence de paires CuI-CuI. Les structures cristallines et magnétiques de plusieurs séries de fluorures ternaires d'éléments de transition ont été déterminées. Les structures sont formées d'un réseau d'octaèdres MF6 liés entre eux de manière 3D, 2D ou 1D. Les structures magnétiques ont été déterminées soit en l'absence de champ magnétique, soit sous un champ pouvant atteindre 6T. Des transitions de type spin-flop caractérisent les composés TIMnIIIF4, xH2O (x=0,1). Une nouvelle variété structurale de la weberite a été caracterisée.